Two-component self-leveling

Uses

M616 two-component self-leveling according to jCT985-2017 and GBT25181-2010 technical requirements. A component and B component fully mixed, with high fluidity and good plasticity, suitable for indoor and outdoor concrete, ceramic tile, steel plate and other base level. For laying all kinds of elastic floor, carpet, wood floor and other decorative materials to provide smooth solid base.

Features

Low ratio of compressive strength to flexural strength, excellent flexibility

Without mixing with water, the construction thickness can be 2mm-8mm

Non-toxic, harmless, green.

Application

1.After the basic treatment, brush the special primer, when the primer is dry, self-leveling can be started. The steel plate base layer shall be coated with "special primer" after rust removal, and shall be self-leveling construction after curing.

2.Pour B component in a container, then slowly to join A component, stirred with mixer for 3-5 minutes , pour the mixture was uniformly spread with a special scraper control the thickness.

3. Before the initial setting of self-levelling, the antifoaming roller is used for antifoaming.

4. The mixture must be used within 20 minutes.

Note

Avoid contact with skin and eyes.

Packaging and Storage

A:25kg/bag,B: 7.8kg/barrel. The product shall be kept indoors , pay attention to moisture , prevent freezing, exposure. Stacked on pallets no more than eight layers , Under the condition of good moisture-proof measures the shelf life of six months.

Mixing ratio :

A：25kg B：7.8kg

Consumption :

Approximately 3.5kg/m2·2mm (in total of two components)

Walkable time:

About 6 hours later

Ratio of compressive strength to flexural strength:

≤3

<div

Substrate Treatment

The base must be dry, firm, load-bearing, dust-free, no obstruction to bonding sundries, smooth surface

Base without hollow drum, with good compressive strength; In order to ensure good adhesion, the base is sealed with primer. M318 water-based primer is recommended for absorbent base and M320 non-absorbent primer is recommended for non-absorbent base.